Surface Finish: |
Polished |
Color: |
White |
Hardness: |
9 Mohs |
Density: |
3.9 G/cm3 |
Dielectric Constant: |
9.8 |
Coefficient Of Thermal Expansion: |
8x10^-6/°C |
Transparency: |
Opaque |
Application: |
Industrial Ceramic |
Alumina Content: |
95% |
Material: |
Alumina |
Wear Resistance: |
Excellent |
Dielectric Strength: |
15 KV/mm |
Electrical Resistivity: |
10^14 Ω·cm |
Maximum Use Temperature: |
1700c |
Water Absorption: |
0 |
Surface Finish: |
Polished |
Color: |
White |
Hardness: |
9 Mohs |
Density: |
3.9 G/cm3 |
Dielectric Constant: |
9.8 |
Coefficient Of Thermal Expansion: |
8x10^-6/°C |
Transparency: |
Opaque |
Application: |
Industrial Ceramic |
Alumina Content: |
95% |
Material: |
Alumina |
Wear Resistance: |
Excellent |
Dielectric Strength: |
15 KV/mm |
Electrical Resistivity: |
10^14 Ω·cm |
Maximum Use Temperature: |
1700c |
Water Absorption: |
0 |
Silicon nitride(Si3N4)exceeds many other ceramic materials in thermal shock-resistance.It does not deteriorate at high temperatures;therefore,it is ideal for use in components for automotive engines and gas turbines-including turbocharger rotors,glow plugs for diesel engines,and hot plugs.Further applications of this material are anticipated in a wide range of fields.