Hardness HRA90-92 Alumina Ceramic Ring

Product Details

Place of Origin: Made In China

Brand Name: Dayoo

Payment & Shipping Terms

Minimum Order Quantity: Negotiable

Price: Negotiable

Delivery Time: Negotiable

Payment Terms: Negotiable

Get Best Price

Product Details

Product Description

Highlight: 
                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                Superior Material Alumina Ceramic, High Electrical Insulation Alumina Ceramic, Mechanical Strength Alumina Ceramic
                              

Transparency:	Opaque	Dielectric Strength:	15 KV/mm
Materials:	92% Alumina Powder	Type:	Ceramic Ball
Material:	Alumina Ceramic	Elastic Modulus:	380 GPa
Shape:	Cylinder	Surface Finish:	Fine
Melting Point:	2,072°C	Precision Tolerance:	High
Compressive Strength:	2000 MPa	Machinability:	Difficult
Application:	Industrial Ceramic	Alumina Content:	92% & 95%

Transparency:	Opaque
Dielectric Strength:	15 KV/mm
Materials:	92% Alumina Powder
Type:	Ceramic Ball
Material:	Alumina Ceramic
Elastic Modulus:	380 GPa
Shape:	Cylinder
Surface Finish:	Fine
Melting Point:	2,072°C
Precision Tolerance:	High
Compressive Strength:	2000 MPa
Machinability:	Difficult
Application:	Industrial Ceramic
Alumina Content:	92% & 95%

Hardness HRA90-92 Alumina Ceramic Ring

Hardness HRA90-92 Alumina Ceramic Ring

[Product Introduction]

This high-precision alumina ceramic ring component (purity ≥95%) is manufactured using isostatic pressing technology, featuring an ivory-white porcelain luster with a precision structure consisting of an annular body and symmetrically distributed grooves. Sintered at 1600°C, the product achieves a density of 3.85g/cm³ with surface roughness Ra≤0.4μm. Rounded edge treatment ensures installation safety, making it suitable for core transmission systems in automation equipment.

[Core Applications]

Precision Machinery: High-speed motor bearing retainers, servo system positioning rings
Electronic Semiconductors: IC test fixture insulation bases, wafer carrier positioning components
New Energy Sector: Lithium battery pole piece cutting dies, hydrogen fuel cell bipolar plate frames
Medical Devices: Minimally invasive surgical instrument guide sleeves, dental implant abutment connectors

[Performance Advantages]

✅ Physical Properties: Hardness HRA90-92 (sapphire-comparable), flexural strength ≥350MPa
✅ Temperature Resistance: Operating range -200°C~1600°C, thermal expansion coefficient 6.8×10⁻⁶/°C
✅ Chemical Stability: Resistant to strong acids/alkalis (except hydrofluoric acid), insulation resistance >10¹⁴Ω
✅ Precision Control: Dimensional tolerance ±0.01mm, geometric tolerance ≤0.02mm

[Specification Parameter Table]

Parameter Item	Index Value	Test Standard
Outer Diameter	φ55±0.02mm	GB/T 2848-2015
Inner Diameter	φ25±0.01mm	GB/T 2848-2015
Thickness	10±0.01mm	GB/T 2848-2015
Groove Quantity	6 sets symmetric	Custom Drawing
Surface Finish	Ra0.4μm	GB/T 1031-2009
Compressive Strength	≥3000MPa	GB/T 4740-1999

[Production Process]

Raw material proportioning → Ball milling → Spray granulation → Isostatic pressing → Degreasing → High-temperature sintering → CNC precision machining → Ultrasonic cleaning → Laser inspection → Vacuum packaging

[Usage Instructions]

Use dedicated ceramic clamping tools during installation to prevent impact damage
Control temperature changes to ≤5℃/min in working environment
Clean with anhydrous ethanol ultrasonic cleaning (power ≤40kHz)
Avoid storage with metal hard objects; use anti-static packaging

[After-Sales Service]

✓ 7-day no-reason return policy (unopened products)
✓ Free replacement for non-human damage within 1-year warranty
✓ Customization service available (MOQ 50 pieces)
✓ Third-party material testing reports (SGS/CTI optional)

[FAQ]

Q: Does the product support high-temperature sterilization?
A: Withstands 134℃ autoclave sterilization (complies with ISO 17665 standard)

Q: Is RoHS certification available?
A: Full product range passes RoHS 2.0 ten-item testing (Report No.: ENV20230615012)

Hardness HRA90-92 Alumina Ceramic Ring 0

Tags:

Alumina Ceramic

Zirconia Ceramics

Silicon Nitride Ceramics

Silicon Carbide Ceramics

Ceramic Beams

Ceramic Arm

Ceramic Nozzles

Hardness HRA90-92 Alumina Ceramic Ring

Superior Material Alumina Ceramic

High Electrical Insulation Alumina Ceramic

Mechanical Strength Alumina Ceramic

[Product Introduction]

[Core Applications]

[Performance Advantages]

[Specification Parameter Table]

[Production Process]

[Usage Instructions]

[After-Sales Service]

[FAQ]

chemical resistance alumina oxide ceramic,

electrical insulation alumina parts,

electrical insulation alumina custom parts

High Wear Chemical Resistance Alumina Ceramic Components

Alumina Ceramic Components Al203 High Electrical Insulation

High Mechanical Strength Alumina Ceramic Components Alumina Aluminium Oxide

Chemical Resistance Alumina Oxide Ceramic

Alumina Ceramic Products Aluminum Oxide High Wear Resistance

Alumina Ceramic Product Material White Alumina Ceramic Parts High Mechanical Strength

Chemical Resistance Alumina Based Ceramics Alumina Al2O3

Alumina Ceramic Essential for High-Performance Industrial Applications

Alumina Material High Alumina Ceramic High Electrical Insulation

Alumina Ceramic High Purity Alumina High Electrical Insulation

Alumina Ceramic Parts High Mechanical Strength

Alumina Ceramic

Zirconia Ceramics

Silicon Nitride Ceramics

Silicon Carbide Ceramics

Ceramic Beams

Ceramic Arm

Ceramic Nozzles